Effects of Denture Cleansers on Heat-Polymerized Acrylic Resin: A Five-Year-Simulated Period of Use

This study evaluated color stability, surface roughness and flexural strength of acrylic resin after immersion in alkaline peroxide and alkaline hypochlorite solutions, simulating a five-year-period of use. Sixty disc-shaped (16x4 mm) and 60 rectangular specimens (65x10x3.3 mm) were prepared from heat-polymerized acrylic resin (Lucitone 550) and assigned to 3 groups (n=20) of immersion (20 min): C1: distilled water; AP: warm water and one alkaline peroxide tablet; SH: 0.5% NaOCl solution. Color data (∆E) were determined by a colorimeter and also quantified according to the National Bureau of Standards units. A rugosimeter was used to measure roughness (μm) and the flexural strength (MPa) was measured using a universal testing machine. Data were evaluated by Kruskal-Wallis followed by Dunn tests (color stability and surface roughness) and by one-way ANOVA and Bonferroni test (flexural strength). For all tests was considered α=0.05. AP {0.79 (0.66;1.42)} caused color alteration significantly higher than C1 {0.45 (0.37;0.57)} and SH {0.34 (0.25;0.42)}. The mean ∆Ε values quantified by NBS were classified as "trace" for C1 (0.43) and SH (0.31) and "slight" for AP (0.96). SH {-0.015 (-0.023;0.003)} caused significantly higher ΔRa than the C1 {0.000 (-0.004;0.010)} and AP {0.000 (-0.009;0.008)} groups. There was no statistically significant difference among the solutions for flexural strength (C1: 84.62±16.00, AP: 85.63±12.99, SH: 84.22±14.72). It was concluded that immersion in alkaline peroxide and NaOCl solutions simulating a five-year of 20 min daily soaking did not cause clinically significant adverse effects on the heat-polymerized acrylic resin.

Este estudo avaliou as alterações de cor, rugosidade de superfície e resistência à flexão de resinas acrílicas após imersão em soluções de peróxido alcalino e hipoclorito alcalino, simulando um período de cinco anos de uso. Sessenta corpos de prova circulares (16 mm x 4 mm) e 60 retangulares (65 mm x 10 mm x 3,3 mm) de resina acrílica termicamente ativada (Lucitone 550) foram distribuídos (n=20) em três grupos de imersão (20 min): C1: água destilada; PA: solução com água morna e uma pastilha de peróxido alcalino; HS: solução de hipoclorito de sódio a 0,5%. A alteração de cor (∆E) foi determinada por meio de colorímetro e também calculada de acordo com unidades da National Bureau of Standards (NBS). Um rugosímetro foi utilizado para mensuração da rugosidade de superfície (μm) e a resistência à flexão (MPa) foi medida utilizando uma máquina universal de ensaios. Os dados foram avaliados pelo teste de Kruskal-Wallis seguido pelo teste de Dunn (estabilidade de cor e rugosidade de superfície) e análise de variância (ANOVA) a um fator seguida pelo teste de Bonferroni (resistência à flexão). Para todos os testes foi considerado α=0,05. PA {0,79 (0,66;1,42)} causou alterações de cor significativamente maiores que C1 {0,45 (0,37;0,57)} e HS {0,34 (0,25;0,42)}. Os valores médios de ∆E quantificados pela NBS foram classificados como "indiciais" para C1 (0,43) e SH (0,31), e "leves" para PA (0,96). O HS {-0,015 (-0,023;0,003)} acarretou maiores valores de ∆Ra que C1 {0,000 (-0,004;0,010)} e PA {0.000 (-0,009;0,008)} Não houve diferença estatística significante entre as soluções para a resistência à flexão (C1: 84,62±16,00, PA: 85,63±12,99, HS: 84,22±14,72). Concluiu-se que imersões em soluções de peróxido alcalino e hipoclorito de sódio simulando imersões diárias de 20 min por um período de cinco anos não causaram efeitos adversos clinicamente significantes sobre a resina acrílica termicamente ativada.

Adverse Effects on PMMA Caused by Mechanical and Combined Methods of Denture Cleansing

This study evaluated the abrasiveness of mechanical and combined methods of denture hygiene, by the analysis of mass loss and surface roughness. Acrylic resin specimens (Plexiglass) were brushed by a tooth brushing machine (Mavtec) with a soft brush (Tek) and water (control) or four dentifrices (Sorriso, Colgate, Polident and Corega) (Experimental groups) for 50 min, representing one year of brushing (mechanical method). After brushing, the specimens were immersed in 0.5% sodium hypochlorite simulating a daily cleaning of 20 min for one year (combined method). Distilled water (23 ºC) was employed as control. The mass loss (g) was analyzed by an analytical balance and the surface roughness (μm) by a rugosimeter. Data were subjected to ANOVA and Bonferroni test (α=0.05). Polident dentifrice showed lowest values of mass loss for both methods (mechanical: -0.0072±0.0017, combined:-0.011±0.002) and the combined method resulted in greater mass loss than the mechanical, except for Corega. For the surface roughness, after the mechanical method, the lowest values were registered for water (-0.007±0.016) and Polident (0.402±0.378); for the combined method, water (-0.063±0.013) showed the lowest values; there was no statistically significant difference between methods. It was concluded that Polident was the less abrasive dentifrice and the association between chemical and mechanical methods increased the mass loss but did not change the surface roughness of specimens.

Este estudo avaliou a abrasividade causada pelos métodos mecânico e combinado de higiene de próteses totais, por meio da análise da perda de massa e rugosidade de superfície. Corpos de prova de resina acrílica (Plexiglass) foram escovados em máquina de escovação (Mavtec) com escova macia (Tek) e água ou dentifrícios (Sorriso, Colgate, Polident e Corega) (Grupos Experimentais) por 50 min, simulando 1 ano de escovação (método mecânico). Após a escovação, os corpos de prova foram imersos em hipoclorito de sódio a 0,5%, simulando imersões diárias de 20 min por 1 ano (método combinado). Água destilada (23 °C) foi empregada como controle. A perda de massa foi analisada por meio de balança analítica de precisão (g) e a rugosidade de superfície por rugosímetro (μm). Os dados foram submetidos à ANOVA e teste de Bonferroni (α=0,05). Em relação à perda de massa, os menores valores foram obtidos para o Polident em ambos os métodos (mecânico: -0,0072±0,0017; combinado: -0,011±0,002) e o método combinado resultou em maior perda de massa que o método mecânico, exceto para o Corega. Para a rugosidade de superfície, após aplicação do método mecânico, os valores mais baixos foram registrados para água (-0,007±0,016) e Polident (0,402±0,378); para o método combinado, os valores mais baixos foram obtidos para água (-0,063±0,013); não houve diferença estatística entre os métodos. Conclui-se que o Polident foi o dentifrício menos abrasivo e que a associação do método químico ao método mecânico aumentou a perda de massa, porém não alterou a rugosidade de superfície dos corpos de prova.

Solução implantossuportada individualizada após agenesia do incisivo lateral e mesialização do canino superior: pilar de zircônia e coroa cerâmica cimentada para pacientes jovens / A customized, implant-supported solution after lateral incisor agenesis and canine orthodontic mesialization: zirconia abutment and cemented ceramic crown for young patients

A reposição de um incisivo lateral superior ausente pode representar um verdadeiro desafio estético. Dentre as opções disponíveis, a instalação de uma prótese unitária implantossuportada proporciona bons resultados, tanto esteticamente, quanto funcionalmente. Assim, o objetivo deste artigo foi apresentar um caso clínico, no qual um paciente com agenesia do incisivo lateral superior teve a reposição deste dente, através de prótese unitária implantossuportada com conexão protética cone-morse e pilar estético de zircônia. Como resultado, foi obtida uma restauração que supriu as necessidades estéticas e funcionais de um paciente jovem.

The replacement of a missing upper lateral incisor can be a real esthetic challenge. Among the available options, the insertion of a single implant-supported prosthesis can provide good results, both aesthetically and functionally. Thus, the purpose of this study is to present a case in which a patient with agenesis of upper lateral incisor received a Cone-Morse connection design with a screwed zirconia abutment and a final cemented crown. In this way, both funcional and esthetic demands were addressed for this young patient.

Morse taper implants at different bone levels: a finite element analysis of stress distribution

Aim: To explore the biomechanical effects of the different implantation bone levels of Morse taper implants, employing a finite element analysis (FEA). Methods: Dental implants (TitamaxCM) with 4x13 mm and 4x11 mm, and their respective abutments with 3.5 mm height, simulating a screwed premolar metal-ceramic crown, had their design performed using the software AnsysWorkbench10.0. They were positioned in bone blocks, covered by 2.5 mm thickness of mucosa. The cortical bone was designed with 1.5 mm thickness and the trabecular bone completed the bone block. Four groups were formed: group 11CBL (11 mm implant length on cortical bonelevel), group 11TBL (11 mm implant length on trabecular bone level), group 13CBL (13mm implant length on cortical bone level) and group 13TBL (13 mm implant length on trabecular bonelevel). Oblique 200 N loads were applied. Von Mises equivalent stresses in cortical and trabecular bones were evaluated with the same design program. Results: The results were shown qualitatively and quantitatively by standard scales for each type of bone. By the results obtained, it can be suggested that positioning the implant completely in trabecular bone brings harm with respect to the generated stresses. Its implantation in the cortical bone has advantages with respect to better anchoring and locking, reflecting a better dissipation of the stresses along the implant/bone interfaces. In addition, the search for anchoring the implant in its apical region in cortical bone is of great value to improve stabilization and consequently better stress distribution.Conclusions: The implant position slightly below the bone in relation to the bone crest brings advantages as the best long-term predictability with respect to the expected neck bone loss.

Problemas na junção implante/prótese: uma alternativa para resolução do caso / Problems at the implant/prosthesis junction: an alternative for solving the case

A Implantodontia vem se destacando entre as diversas áreas da Odontologia moderna. As possibilidades de tratamento envolvendo os implantes dentários têm facilitado e ampliado a gama de opções ao cirurgião dentista. No entanto, a proposta de tratamento envolvendo reabilitação sobre implantes traz consigo problemas a serem solucionados, já que tal tratamento também é passível de intercorrências. A curva de aprendizagem com o emprego da Implantodontia deve ser respeitada, já que tanto na fase cirúrgica quanto na fase protética, existem critérios a serem respeitados para um bom prognóstico do tratamento. Além disso, quando surgem as intercorrências é imprescindível o preparo e conhecimento do profissional em questão. O presente caso clínico relata uma reabilitação unitária sobre implante, a qual necessitou ser realizada fora dos padrões normais da Implantodontia, já que foi constatada deformação na plataforma hexagonal do mesmo. É possível que tal ocorrência tenha sido causada na fase cirúrgica, durante a instalação do implante, devido a um provável torque excessivo, resultando na impossibilidade da adaptação dos componentes protéticos. A resolução do caso ocorreu com a instalação de um núcleo metálico fundido sobre o implante e confecção de prótese metalocerâmica cimentada. Com o presente relato, pode-se notar a importância do conhecimento de conceitos básicos por parte do cirurgião dentista, assim como sua flexibilidade frente às intercorrências do tratamento

The Implantology has become highlighted among the various areas of modern dentistry. The treatment possibilities involving dental implants have facilitated and expanded the range of options to the dentist. However, the treatment involving rehabilitation with implants can bring problems to be solved, as this treatment is also susceptible to complications. Learning curve with the use of implants should be respected, both in the surgical and prosthetic phases, because there are criteria to be met for a good treatment prognosis. Also, when complications occur, it is essential preparation and knowledge of the professional. This case report describes unit rehabilitation with implant, which needed to be performed outside of the normal standards of implant dentistry, as was observed deformation on the hexagonal platform. It is possible that it has been caused during implant installation surgery phase, due to an excessive torque, resulting in the inability to adapt the prosthetic components. The case resolution was with the installation of a cast metal core on the implant and making a metaloceramic cemented prosthesis. With this case report may be noted the importance of knowledge of basic concepts by the dentist, as well as its flexibility in the face of complications of treatment

Abrasiveness of conventional and specific denture-cleansing dentifrices

This study analyzed the weight loss and surface roughness caused in Plexiglass specimens by conventional dentifrices (Sorriso, Colgate and Close Up) and specific dentifrices used for cleaning of dentures (Corega and Dentu Creme). Plexiglass specimens were divided into 6 groups (n=6) including: a control (distilled water - DW) and experimental groups. Brushing was performed in a toothbrushing machine with a soft brush and a dentifrice suspension and DW according to different brushing times (50, 100, 200 and 250 min -18,000, 36,000, 72,000 and 90,000 cycles, respectively, calculated to correspond to 1, 2, 4 and 5 years of regular brushing). The results of weight loss and surface roughness were analyzed by ANOVA and Tukey’s test at 5% significance level. In all tested times, the effect of DW was insignificant. Dentifrices differed significantly from DW in the initial period. Corega dentifrice caused greater mass loss in all studied times, followed by Close Up. Dentifrices resulted in a surface roughness similar to the DW at 50 min. In the other times, Sorriso, Colgate and Corega caused more surface roughness than DW. In conclusion, specific dentifrices caused larger mass loss and lower surface roughness as conventional dentifrice.

Este estudo analisou a perda de massa e rugosidade superficial causadas em corpos de prova de Plexiglass por dentifrícios convencionais (Sorriso, Colgate e Close Up) e específicos (Corega e Dentu Creme) para higienização de próteses totais. Os corpos de prova de Plexiglass foram distribuidos em 6 grupos (n=6), sendo um controle (água destilada - AD) e grupos experimentais. A escovação foi realizada em máquina de escovação com escovas macias e suspensões de dentifrícios ou AD, de acordo com os diferentes tempos de escovação (50, 100, 200 e 250 min -18.000, 36.000, 72.000 e 90.000 ciclos, respectivamente, calculados para corresponder a 1, 2, 4 e 5 anos de escovação regular). Os resultados de perda de massa e rugosidade superficial foram analisados por meio de ANOVA e teste de Tukey com 5% de significância. Em todos os tempos analisados, a AD teve efeito insignificante. Os dentifrícios diferiram significativamente da AD no período inicial. O dentifrício Corega causou maior perda de massa em todos os tempos estudados, seguido por Close Up. No tempo de 50 min, todos os dentifrícios causaram rugosidade superficial semelhante à AD. Nos outros tempos, Sorriso, Colgate e Corega causaram maior rugosidade superficial em relação à AD. Conclui-se que os dentifrícios específicos causaram maior perda de massa, porém menor rugosidade superficial que os dentifrícios convencionais.